Growth and laser properties of laser crystal Nd: Gd0.8La0.2VO4

Huaijin Zhang; Xianlin Meng; Li Zhu; Changqing Wang; Pu Wang; Hongzhen Zhang; Y. T. Chow; Judith Dawes

doi:10.1016/S0022-0248(98)00495-3

Growth and laser properties of laser crystal Nd: Gd0.8La0.2VO4

Huaijin Zhang, Xianlin Meng, Li Zhu, Changqing Wang, Pu Wang, Hongzhen Zhang, Y. T. Chow, Judith Dawes

MQ Photonics Research Centre

Research output: Contribution to journal › Article › peer-review

11 Citations (Scopus)

Abstract

Nd : Gd_0.8La_0.2VO₄ single crystal with zircon structure was successfully grown by the Czochralski method, and the lattice constants are a = b = 0.7239(1) nm, c = 0.6360(1) nm. The polarization absorption spectra were measured from 400 to 850 nm, the polarization emission spectra from 1053 to 1075 nm are measured. 948 mW power laser at 1.06 μm was achieved with 1 mm thick Nd : Gd_0.8La_0.2VO₄ crystal sample when pumped by a 1.9 W cw laser diode.

Original language	English
Pages (from-to)	370-373
Number of pages	4
Journal	Journal of Crystal Growth
Volume	193
Issue number	3
DOIs	https://doi.org/10.1016/S0022-0248(98)00495-3
Publication status	Published - 1 Oct 1998

Keywords

Crystal growth
Laser performance
Nd : GdLaVO crystal
Spectroscopy

Access to Document

10.1016/S0022-0248(98)00495-3

Cite this

@article{1cb00cdbb9804ec5959e23cab069cbc0,

title = "Growth and laser properties of laser crystal Nd: Gd0.8La0.2VO4",

abstract = "Nd : Gd0.8La0.2VO4 single crystal with zircon structure was successfully grown by the Czochralski method, and the lattice constants are a = b = 0.7239(1) nm, c = 0.6360(1) nm. The polarization absorption spectra were measured from 400 to 850 nm, the polarization emission spectra from 1053 to 1075 nm are measured. 948 mW power laser at 1.06 μm was achieved with 1 mm thick Nd : Gd0.8La0.2VO4 crystal sample when pumped by a 1.9 W cw laser diode.",

keywords = "Crystal growth, Laser performance, Nd : GdLaVO crystal, Spectroscopy",

author = "Huaijin Zhang and Xianlin Meng and Li Zhu and Changqing Wang and Pu Wang and Hongzhen Zhang and Chow, {Y. T.} and Judith Dawes",

year = "1998",

month = oct,

day = "1",

doi = "10.1016/S0022-0248(98)00495-3",

language = "English",

volume = "193",

pages = "370--373",

journal = "Journal of Crystal Growth",

issn = "0022-0248",

publisher = "Elsevier",

number = "3",

}

TY - JOUR

T1 - Growth and laser properties of laser crystal Nd: Gd0.8La0.2VO4

AU - Zhang, Huaijin

AU - Meng, Xianlin

AU - Zhu, Li

AU - Wang, Changqing

AU - Wang, Pu

AU - Zhang, Hongzhen

AU - Chow, Y. T.

AU - Dawes, Judith

PY - 1998/10/1

Y1 - 1998/10/1

N2 - Nd : Gd0.8La0.2VO4 single crystal with zircon structure was successfully grown by the Czochralski method, and the lattice constants are a = b = 0.7239(1) nm, c = 0.6360(1) nm. The polarization absorption spectra were measured from 400 to 850 nm, the polarization emission spectra from 1053 to 1075 nm are measured. 948 mW power laser at 1.06 μm was achieved with 1 mm thick Nd : Gd0.8La0.2VO4 crystal sample when pumped by a 1.9 W cw laser diode.

AB - Nd : Gd0.8La0.2VO4 single crystal with zircon structure was successfully grown by the Czochralski method, and the lattice constants are a = b = 0.7239(1) nm, c = 0.6360(1) nm. The polarization absorption spectra were measured from 400 to 850 nm, the polarization emission spectra from 1053 to 1075 nm are measured. 948 mW power laser at 1.06 μm was achieved with 1 mm thick Nd : Gd0.8La0.2VO4 crystal sample when pumped by a 1.9 W cw laser diode.

KW - Crystal growth

KW - Laser performance

KW - Nd : GdLaVO crystal

KW - Spectroscopy

UR - http://www.scopus.com/inward/record.url?scp=0032182817&partnerID=8YFLogxK

U2 - 10.1016/S0022-0248(98)00495-3

DO - 10.1016/S0022-0248(98)00495-3

M3 - Article

AN - SCOPUS:0032182817

SN - 0022-0248

VL - 193

SP - 370

EP - 373

JO - Journal of Crystal Growth

JF - Journal of Crystal Growth

IS - 3

ER -

Growth and laser properties of laser crystal Nd: Gd0.8La0.2VO4

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this