T1 - Preparation and study of bi-supported Ziegler-Natta catalyst with nano graphene oxide and magnesium ethoxide supports for polymerization of polyethylene
AU - Kheradmand, Amanj
AU - Abadi, Ahmad Ramazani Saadat
AU - Khorasheh, Farhad
AU - Baghalha, Morteza
AU - Bahrami, Hiva
PY - 2016/5
Y1 - 2016/5
N2 - In this study, we have reported the preparation of bi-supported Ziegler-Natta catalysts using magnesium ethoxide and graphene oxide as support. The polymerization process was carried out in slurry phase using triisobutylaluminum as a co-catalyst.The XRD analysis of TiCl4/graphene oxide/Mg(OEt)2 catalyst demonstrated that the space between the layers of graphene oxide had increased to 0.2 nm.The catalyst was characterized by XPS, BET, BJH, SEM, and TGA. The catalyst activity was studied for various Al/Ti molar ratios, and the catalyst activity was optimum at Al/Ti molar ratio of 315.
AB - In this study, we have reported the preparation of bi-supported Ziegler-Natta catalysts using magnesium ethoxide and graphene oxide as support. The polymerization process was carried out in slurry phase using triisobutylaluminum as a co-catalyst.The XRD analysis of TiCl4/graphene oxide/Mg(OEt)2 catalyst demonstrated that the space between the layers of graphene oxide had increased to 0.2 nm.The catalyst was characterized by XPS, BET, BJH, SEM, and TGA. The catalyst activity was studied for various Al/Ti molar ratios, and the catalyst activity was optimum at Al/Ti molar ratio of 315.
UR - http://www.scopus.com/inward/record.url?scp=84964321035&partnerID=8YFLogxK
U2 - 10.1134/S156009041603009X
DO - 10.1134/S156009041603009X
M3 - Article
VL - 58
SP - 271
EP - 277
JO - Polymer Science - Series B
JF - Polymer Science - Series B
SN - 1560-0904
IS - 3
ER -